A STUDY OF SURFACE EXPULSION PHENOMENA AND ITS SUPPRESSION IN SERIES SPOT WELDING. BADANIA NAD POWSTAWANIEM POWIERZCHNIOWYCH WYPRYSKOW I ZAPOBIEGANIEM ICH WYSTEPOWANIU PRZY ZGRZEWANIU DWUSTRONNYM. TRANS.J.W.S. 1980, NR 2, S. 72-79, 4 FOT., 12 RYS., BIBLIOGR. 8 POZ.

NA STALI NISKOWEGLOWEJ O GRUBOSCI 0.8 MM PRZEPROWADZONO BADANIA MAJACE NA CELU UZYSKANIE PRZY ZGRZEWANIU DWUPUNKTOWYM GESTOSCI PRADU UMOZLIWIAJACYCH UTWORZENIE JADRA O WYMIARACH JAK W PRZYPADKU ZGRZEWANIA JEDNOPUNKTOWEGO, JEDNAK BEZ POWIERZCHNIOWYCH WYPRYSKOW. STWIERDZONO, ZE PRZYCZYNA POWSTAWANIA POWIERZCHNIOWYCH WYPRYSKOW PRZY DWUSTRONNYM ZGRZEWANIU DWUPUNKTOWYM JEST WYPLYWANIE CIEKLEGO METALU Z JADRA PRZEZ PRZEGRZANY METAL WSKUTEK BOCZNIKOWANIA PRADU PRZEZ GORNA BLACHE. ZJAWISKO TO ZACHODZI NAWET PRZY GESTOSCIACH PRADU NIZSZYCH OD STOSOWANYCH PODCZAS ZGRZEWANIA JEDNOPUNKTOWEGO. ZASTOSOWANIE GORNYCH ELEKTROD O WIEKSZEJ POWIERZCHNI CZESCI ROBOCZEJ W POROWNANIU DO ELEKTROD DOLNYCH UMOZLIWIA STOSOWANIE WYZSZYCH WARTOSCI PRADU ZGRZEWANIA BEZ POWSTAWANIA WYPRYSKOW.
http://lib.is.gliwice.pl/library/catalog/item?query=klucz:"K...

cc
Expulsion and its influence on weld quality.
Przeprowadzono szereg prób zgrzewania w celu określenia wpływu wyprysku metalu przy zgrzewaniu na jakość i własności zgrzein. Badania wykazały, że wypryski metalu przy zgrzewaniu mogą wpłynąć niekorzystnie zarówno na własności mechaniczne zgrzein jak i na ich estetykę. Dokonano przeglądu różnych modeli wspomagających przewidywanie wystąpienia wyprysku przy danych parametrach. Prawdopodobieństwo wystąpienia wyprysku zostało przedstawione graficznie jako funkcja prądu zgrzewania, czasu i siły docisku elektrod.

WYPRYSK ZGRZEINY, CZYNNIK WPŁYWAJĄCY, JAKOŚĆ, WYGLĄD, ZGRZEINA